Chrome free Zinc Flake Coating For Brake Disc JH-310, Zinc flake coating Manufacturer And Metal Coating Company

Home
>
Chemical
>
Zinc flake coating
>
Chrome free Zinc Flake Coating For Brake Disc JH-310

Chrome free Zinc Flake Coating For Brake Disc JH-310

Product Details:
Brand Name: JUNHE
Model Number: JH-310

Inquiry

Description
Coating Process
Mix Diagram
Attentions
Technical data
left
right

Description:

JH-310is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

Performance Charcteristic:

Chrome free , film is silver grey to silver white, better corrosion protection performance.Environmentally friendly products, film is silver, has good corrosion resistance, the use of technology is almost equivalent to the JUNHE of dacroment.

Coating Process:

1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )

2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

3. Add B to the stirring A slowly.

4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 20℃, otherwise C will not be dissolved sufficiently .)Then stir 10~12 hours alowly and continuously.

Chrome free Zinc Flake Coating For Brake Disc JH-310

Mix Diagram:

Attentions:

1. Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

2. Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

3. It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.

4. The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.

Technical data:

No.	Item	Data
1	Color	Silver
2	Coating method	Spraying
3	PH	4.8-7.5
4	Specific gravity	1.45±0.1
5	Viscosity	25~40s(Spray Coating)

Minimum Order Quantity: 100 Kiloamperes
Packaging Details: Pack A:20kg/ Metal Barrel
Pack B:20KG Plastic Barrel
Pack C:Based on the amount of B agent A
Delivery Time: Ten days after receipt of advance payment
Payment Terms: L/C, T/T
Supply Ability: 2 Ton/Tons per Day

Color: Silver
Coating Method: Spraying
PH(20℃): 4.8-7.5
Specific Gravity: 1.45±0.1
Viscosity: 25~40s(Spray Coating)
Operating Temperature: 24±4℃

Related Products

Chrome Free Water Based Zinc Flake Coating Salt Fog Time 480 Hours JH-9310

Chrome free water based zinc flake coating Salt fog time 480 hours PH ( 20℃ ) 5.0-8.0 Product Description JH-9310 is made up of three packs: A,B and C; Pack A: It is silver gray slurry that mainly chemically ...

Chrome Free Zinc Flake Coating JH-9610

Chrome free water base zinc flake coating paint Silver Color PH ( 20℃ ) 5.0 - 8.0 Product Description JH-9610is made up of three packs: A,B and C;Pack A: It is silver gray slurry that mainly chemically combined ...

Silver Color Zinc Flake Coating JH-9630

Chrome free water base zinc flake coating paint Silver Color PH ( 20℃ ) 5.0 - 8.0 Product Description JH-9630is made up of three packs: A,B and C;Pack A: It is silver gray slurry that mainly chemically combined ...

Water-base Microlayer Corrosion Protection Coating (chrome free)

Zincover-9318

Chrome free , film is silver grey to silver white, better corrosion protection performance.

Chrome free Zinc Flake Coating For Brake Disc JH-310

Related Products

follow us

newsletter