Description:

JH-9510 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

Performance characteristics:

The film is silver white, good surface finish, high corrosion resistance, and then good friction coefficient of small 0.12-0.18.

Coating Process:

1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )

2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃, then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

3. Add B to the stirring A slowly.

4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours alowly and continuously.

5. The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.

6. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.
(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

7. Test Specific gravity, PH, Temperature, Viscosity of coating every 8 hours if operate continuously.

Mix Diagram:

Attentions:

Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature, viscosity and spinning process shoud be controlled well when coating.

The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data
if dip spin coating.

Technical data:

No.	Item	Data
1	Color	Silver
2	Coating method	Dip Spin & Spraying
3	PH	3.8-5.2
4	Specific gravity	1.33±0.05 (spray coating) 1.33±0.05(dip-spin coating)
5	Viscosity	20~60seconds(spray coating) 60-80seconds(dip-spin coating)
6	Operating temperature	20±2℃

Payment & Shipping Terms:
Minimum Order Quantity: 100 Kilograms
Packaging Details: Pack A:16kg/ Metal Barrel
Pack B:24KG Plastic Barrel
Pack C:Based on the amount of B agent A
Delivery Time: Ten days after receipt of advance payment
Supply Ability: 2 Tons per Day

Coating Method: Dip Spin & Spray
Color: Silver
PH: 3.8-5.2
Specific Gravity: 1.33±0.05 (spray Coating) 1.33±0.05(dip-spin Coating)
Viscosity: 20~60seconds(spray Coating) 60-80seconds(dip-spin Coating)
Operating Temperature: 20±2℃

Related Products

Self Dry Silver Top Coat JH-9320

Self dry silver top coat dacromet coating surface coating PH 3.8-5.2 coating thickness(μ) ≥15 Product Description Our for zinc flake coating surface hardness is low, defects in the coating and acid and alkali ...

Black Dacromet Coating Paint Top Coat JH-9321

Black matte water base top coat PH 8.0-9.0 Thickness of dry film 10-20 (micron) Product Description 1) The main ingredient is water-base inorganic silica , mixed with corrosion protection assistant. 2) The ...

Dacromet Coating Transparent Top Coat JH-9323

Dacromet special transparent surface coating PH 8.0-9.0 Resistance to hot and humid 240 ( h ) Product Description This product applies to steel, cast iron, aluminum, iron base powder metallurgy, etc. The ...

Silver Dacromet Coating Nano Alloy Coating High Corrosion Resistance JH-9088

JH-9088 High Corrosion Resistance Nanometer Alloy Coating Density 0.9-1.2g/ml 1 Product Information According to the galvanized coating have poor corrosion resistance and defect of acid and alkali resistant,our ...

Low Friction Dacromet Coating Friction Paint JH-9510

Related Products

follow us

newsletter