High quality Very first,and Consumer Supreme is our guideline to offer the most beneficial service to our consumers.At present, we're attempting our greatest to be among the top exporters in our area to fulfill buyers far more need to have for Protective Clear Coat For Latex Paint, Anticorrosion Coatings, Galvanizing Touch Up Paint, With advantage of industry management, the business has generally been committed to supporting prospects to become the current market leader in their respective industries.

100% Original Hot Dip Zinc Coating - Zincover® 9730 Water-base Chrome-free Zinc Flake Coating – Junhe Detail:

Product Profile

Zincover^®9730 is water-base chrome-free zinc flake coating paint,independently developed by Junhe.It does not contain heavy metal ions,meets RoHS standard,meets the requirements of China EnvironmentalProtection Law,no heavy metal emission,suitable for various fasteners and hardwares.Excellent anti-corrosion coating property. The paint has excellent salt spray resistance and strong adhesion ability,which meets thecoating standard requirements of fasteners and hardware parts of most auto companies.

FunctionalProprty

1、 Safety and environmental friendly: water-based,low VOC,no heavy metal,in line with GB24409 – 2020 GB30981 – 2020 GB / T18178 – 2020 GB30981 – 2020,also meeting the instruction requirement of EU RoHS ( 2002 / 95 / EC ) and ELV ( 2000 / 53 / EC ).

2、Excellent anti-corrosion property:

Thickness of coating layer	Coating amount	Salt-spray Test（ISO9227/ASTM B117）
12~15μm	≥240 mg/ dm²	1000h no red rust
13~18μm	≥240mg/ dm² base coat+ Zincover^® 9130 top coat	≥1600h no red rust（top coat 1~3μm）

3、Wide coating Proces range: dip spin coating,spray coating and Leaching.
4、Wide functional properties: coating layer resists 400 °C high temperature,no hydrogen embrittlement,strong recoatability.
5、Long storage time: after mixing part A and part B,stirring at 20-25 °C,the performance loss is less than 20% within 20 days.

Technical Parameter

Density	1.3~1.4g/ml	Ø800 centrifugal speed	230~300 rpm/min
Solid content	38~40%	Use viscosity(Zahn Cup #2)	Dip spin: 60~80s,spraying: 30~60s,leaching: 20~40s
Finess	＜20μm	Pre-heating/Time	20±10℃/more than10min
Viscosity(Zahn Cup #2)	20~30（A+B)	Curing /Time	320±10℃/more than 20min

*These properties may vary depending on the substrate,process,batch and workpiece shape.

Application Field

Anti-corrosion coating of fasteners and hardware Components in automobile,wind power,photovoltaic andhigh speed railway industry.

Changzhou Junhe Technology Stock Co.,Ltd
Website:www.junhetec.com Email: marketing@junhe-china.com
Tel:86-519-85922787 Mobile: 13915018025

Product detail pictures:

Related Product Guide:

We have been ready to share our knowledge of internet marketing worldwide and recommend you suitable merchandise at most aggressive rates. So Profi Tools present you very best price of money and we are ready to develop alongside one another with 100% Original Hot Dip Zinc Coating - Zincover® 9730 Water-base Chrome-free Zinc Flake Coating – Junhe , The product will supply to all over the world, such as: Sydney, Vietnam, Ethiopia, We will not only continuously introduce technical guidance of experts from both home and abroad, but also develop the new and advanced products constantly to satisfactorily meet the needs of our clients all over the world.

Aluminium Protective Coating

Bitumen Pipe Coating

Flake Zinc Coating

Metal Zinc Coating

Protective Paint Coating

Tablet Coating Machine Parts

Undercoating Paint Over Rust

Zinc Coating Rust

Zinc Dichromate Coating

Zinc Flake Coating Process

Hope that the company could stick to the enterprise spirit of "Quality, Efficiency, Innovation and Integrity", it will be better and better in the future.